Аннотация:
Based on the results of X-ray phase analysis and Mössbauer spectroscopy, it was demonstrated that in the ZrO$_2$–Fe$_2$O$_3$ system, represented by the mechanical mixture of $m$–ZrO$_2$ ($14\pm 2$ nm) and $\alpha$-Fe$_2$O$_2$ ($43\pm 2$ nm) nanoparticles, being heated above the temperature corresponding to the melting temperature of the two-dimensional nonautonomous phase, transformation of $\alpha$-Fe$_2$O$_2$ occurs resulting in appearing of the X-ray amorphous magnetically disordered state localized on the surface of ZrO$_2$ nanoparticles in the form of a thin layer. Transformation pattern in ZrO$_2$–Fe$_2$O$_3$ nanocrystalline system has been introduced.
This work was supported by Ministry of education and science of the Russian Federation (Project 3.6522.2017).
Поступила в редакцию: 02.10.2018 Исправленный вариант: 24.11.2018
Реферативные базы данных:
Тип публикации:
Статья
PACS:
64.75.+g; 76.20.+q
Язык публикации: английский
Образец цитирования:
S. A. Kirillova, O. V. Almjasheva, V. V. Panchuk, V. G. Semenov, “Solid-phase interaction in ZrO$_2$–Fe$_2$O$_3$ nanocrystalline system”, Наносистемы: физика, химия, математика, 9:6 (2018), 763–769
\RBibitem{KirAlmPan18}
\by S.~A.~Kirillova, O.~V.~Almjasheva, V.~V.~Panchuk, V.~G.~Semenov
\paper Solid-phase interaction in ZrO$_2$–Fe$_2$O$_3$ nanocrystalline system
\jour Наносистемы: физика, химия, математика
\yr 2018
\vol 9
\issue 6
\pages 763--769
\mathnet{http://mi.mathnet.ru/nano367}
\crossref{https://doi.org/10.17586/2220-8054-2018-9-6-763-769}
\isi{https://gateway.webofknowledge.com/gateway/Gateway.cgi?GWVersion=2&SrcApp=Publons&SrcAuth=Publons_CEL&DestLinkType=FullRecord&DestApp=WOS_CPL&KeyUT=000455960100009}
\elib{https://elibrary.ru/item.asp?id=36654087}
Образцы ссылок на эту страницу:
https://www.mathnet.ru/rus/nano367
https://www.mathnet.ru/rus/nano/v9/i6/p763
Эта публикация цитируется в следующих 1 статьяx:
Ali Sari, Mourad Keddam, Abdelkader Ouanezar, Abderrahim Malki, “Investigation on structural and magnetic properties of the mechanosynthesized Fe-doped ZrO2-15mol”, PAC, 18:4 (2024), 386
Цитирование в формате AMSBIB
Обратная связь: