Аннотация:
Current–voltage characteristics of nanostructured vanadium oxide bronze β-NaV6O15 obtained from oxalate solutions by ultrasonic spray pyrolysis (USP) under various conditions were studied. The conditions of USP synthesis significantly affected the particle morphology, specific surface area, defect structure and oxidizing ability of the compound.
Образец цитирования:
O. I. Gyrdasova, E. V. Vladimirova, L. Yu. Buldakova, M. Yu. Yanchenko, A. V. Dmitriev, “Effect of synthesis conditions on morphology, crystal structure and electrochemical properties of β-NaV6O15”, Mendeleev Commun., 33:3 (2023), 368–371
Образцы ссылок на эту страницу:
https://www.mathnet.ru/rus/mendc400
https://www.mathnet.ru/rus/mendc/v33/i3/p368
Эта публикация цитируется в следующих 2 статьяx:
O. I. Gyrdasova, R. F. Samigullina, E. V. Vladimirova, I. S. Medyankina, L. Yu. Buldakova, M. Yu. Yanchenko, L. A. Pasechnik, “Precursor method for the synthesis of highly dispersed ZrO2 doped with scandium”, Mendeleev Commun., 34:5 (2024), 640–642
V. P. Tolstoy, D. V. Danilov, A. A. Meleshko, “Effect of the formation of open microcapsules with Mn3O4 walls during hydrolysis of the MnSO4 salt solution droplets deposited on the alkaline solution surface”, Mendeleev Commun., 34:3 (2024), 430–432
Обратная связь: